    Investigation of the compressive strength of ntawo ball clay fired to different temperatures at different rates of temperature rise
    (Kyambogo University (un published work), 2017-12) Byekwaso, Ronald
    This study was to investigate the compressive strength of fired Ntawo Ball Clay found in Mukono District in Central Uganda. The clay sample was first analyzed using X-ray Diffraction Spectrometer Model RIX3000 to determine the relative abundance of the chemical components and then compressive strengths were determined. Ball clay of particle size 45.0 μm was used to produce 150 rectangular clay slabs fired in an electric furnace, model P59 l 0. They were then subjected to compressive strength test by first determining the breaking force for each sample using a compressive test machine, compact 500Sn-12994917 on samples fired at different rates of temperature rise, ranging between 2°C min- 1 and 6°C min-1 in intervals of 1°C min-1 for set firing temperatures. The compressive strength tests were then carried out on another set of samples fired at set rates of temperature rise to different firing temperatures ranging between 500°C and I 000°C in intervals of I 00°C. The compressive strength of fired tawo ball clay was found to decrease with increase in rates of temperature rise between 2°Cmin-1 and 6°Cmin-1 for the six firing temperatures. For temperatures of 500°C to I 000°C in intervals of I 00°C, the percentage decrease in compressive strength ' ere 11 %, 3%. 3%. 8%, 2.9%, and 11 % respectively. At a level of significance a = 0.05 and a = 0.0 I, it was established that compressive strength was related to the rate of temperature rise. The study further revealed that compressive strength increased with increase in firing temperature. The percentage increase was 279%, 273%, 247%, 257% and 279% for the rates of temperature rise between 2°Cmin-1 and 6°Cmin-1 respectively, overall average percentage increase being 267%. At a level of significance a= 0.05 and a = 0.0 I, compressive strength depended on firing temperature ntawo clay was found to be composed of mainly silica (67.20%), alumina ( 18.20%), ferrous oxides (2 .83%) and other fluxing oxides such as CaO (0.31 %). K20 (0.98%), and a20 (0. 19%), among other compounds. The compressive strength of fired samples decreased with increase in rates of temperature rise during firing between 500°C and I 000°C. Other investigations should be made to find out the effect of firing beyond I 000°C and firing at a rate above 6°C min1 on the compressive strength, and the effect of changing the mineralogical composition of clay on the compressive strength.